The use of stainless steel pipes is now more and more extensive. Because of its good corrosion resistance, it plays a crucial role in engineering construction. In the process of production, we need to perform solution treatment on stainless steel pipes. The main purpose is to obtain certain Martensite increases the hardness of the product. Let's take a look at the solution treatment of stainless steel pipes:
(1) The intermediate aging method is heated to (760±15) degree after the solution treatment, and the temperature is kept for 90 minutes because Cr23C6 carbides are precipitated from the austenite, which reduces the carbon and alloying elements content in the austenitic 904L stainless steel pipe , the Ms point is raised to 70 degree and then cooled to room temperature to obtain martensite plus ferrite plus retained austenite structure, and the retained austenite is decomposed after aging at 510 degree .
(2) Después del ajuste de alta temperatura y el tratamiento criogénico, la solución primero se calienta a 950 grados durante 90 minutos. Debido al aumento del punto Ms, se puede obtener una pequeña cantidad de martensita enfriando a temperatura ambiente; cantidad de martensita.
(3) Después del tratamiento de solución por el método de deformación en frío, la deformación en frío se realiza a temperatura ambiente. La cantidad de martensita formada en la tubería sin costura 904L durante la deformación en frío está relacionada con la cantidad de deformación y la composición de la tubería de acero inoxidable 904L.
Los tres métodos anteriores son métodos comúnmente utilizados para el tratamiento de solución de tuberías de acero inoxidable. Espero que puedan ayudarte.